Sign In | Join Free | My remastersys.com
China HLS Coatings (Shanghai)Co.Ltd logo
HLS Coatings (Shanghai)Co.Ltd
HAOLISEN – Innovative Material Future
Verified Supplier

7 Years

Home > Low Temperature Curing Electrophoresis Paint >

Easy Coat Low Temperature Curing Electrophoresis Paint For Compressor

HLS Coatings (Shanghai)Co.Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment

Easy Coat Low Temperature Curing Electrophoresis Paint For Compressor

  • 1
  • 2

Brand Name : HAOLISEN

Model Number : OHT-825/OHT-825

Certification : IATF16949 , ISO9001

Place of Origin : Shanghai China (Mainland)

MOQ : Negotiation

Price : Negotiation

Supply Ability : 200 Tons Per Day

Delivery Time : 30-60 Days

Packaging Details : 50kg、60 kg、200kg、1000kg packaging barrels

Application field : Compressor

main ingredients : Alcohol ether

Performance : Good salt mist

Cooperation case : HUAYI,QIANGJIANG

Contact Now

Low temperature curing electrophoresis paint for Compressor

Product Introduction :

OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation of independent research and development of electrophoretic coating. The lead, cadmium, chromium, mercury and other heavy metals, two-component aqueous dispersion resin. At the same time, inherited the characteristics of several generations of product quality, OHT-825 on galvanized steel sheet has good adaptability, almost at the bottom of all the metal material coating,

such as: cold rolled steel, galvanized steel, aluminum, stainless steel plate, rubber parts, zinc and aluminum alloy plate, such as applicable

.

This product features shown below : 

Good stability of bath can adaptable for a longer updating cycle

High penetration and good uniformity of internal and external.

Particularly suitable for high temperature baking of the workpiece, in particular, rubber and metal binding parts and zinc aluminum alloy material

Main ingredients:

Additives: surface active agent, prevent shrinkage cavity agent

Pigment: carbon black, kaolin, antirust pigment

Neutralizing agent: organic acid

Matrix resin: Acrylic modified epoxy resin

Filling tank proportion and method :

⑴ Bath preparation

Ratio:

Resin 1000.00 -1250.00

Paste 250.00

DI water 1000.00


Total 2250.00 -2500.00

(2)Ripening conditions

Sample quantity: 2250~2500g
Container: 4L (Diameter 16cm)

Tank temperature: 28~32℃

Time: 24~48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)


(3) Coating conditions

Experimental panel: phosphated cold-rolled steel plate

Tank temperature: 28-35℃

Pole ratio: A/C = 1/2 ~ 1/4

Distance of electrodes: 15cm

ED time: For full immersing 1-3 minutes ( 20 seconds soft start)

Baking conditions: (130-140)℃×(20-30)min (Keeping temperature of parts coated)


Specification statement

This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.

If you want to learn more about HLS coating products, please contact Sales Department of Shanghai HLS now

Customer production site :

Easy Coat Low Temperature Curing Electrophoresis Paint For Compressor


Product Tags:

edp painting

      

anti rust coating for cars

      
Cheap Easy Coat Low Temperature Curing Electrophoresis Paint For Compressor for sale

Easy Coat Low Temperature Curing Electrophoresis Paint For Compressor Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: HLS Coatings (Shanghai)Co.Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)